【国外标准】 Standard Specification for Nickel-Iron-Chromium Alloy Seamless Pipe and Tube

This specification covers the standard requirements for nickel-iron-chromium alloy which include UNS N08120, UNS N08800, UNS N08801, UNS N08810, UNS N08811, UNS N08890, and UNS N06811 in the form of cold-worked and hot-finished annealed seamless pipe and tube. The materials shall be heat treated at certain annealing temperatures and shall conform to the chemical composition limits for nickel, chromium, iron, manganese, carbon, copper, silicon, sulfur, aluminum, titanium, columbium, molybdenum, niobium, tantalum, phosphorus, tungsten, cobalt, nitrogen, and boron. Planimetric method of measurement and tension test shall be conducted in full tubular size, longitudinal strip, or round specimens in the direction of fabrication to determine the grain size and mechanical properties, respectively. These materials shall conform to the specified grain size, yield strength, tensile strength, and elongation requirements. Each pipe or tube shall be subjected to hydrostatic or nondestructive eddy-current tests to determine the allowable fiber stress and to detect significant discontinuities such as drilled hole and transverse tangential notch. The cold-drawn material shall be commercially straight, uniform in quality and temper, smooth, and free of bends, kinks, and other injurious imperfections.1.1 This specification2 covers UNS N08120, UNS N08800, UNS N08801, UNS N08810, UNS N08811, UNS N08890, and UNS N06811 in the form of cold-worked and hot-finished annealed seamless pipe and tube. Alloys UNS N08800 and UNS N06811 are normally employed in service temperatures up to and including 1100 °F (593 °C). Alloys UNS N08120, UNS N08810, UNS N08811, and UNS N08890 are normally employed in service temperatures above 1100 °F (593 °C) where resistance to creep and rupture is required, and they are annealed to develop controlled grain size for optimum properties in this temperature range.1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.1.3 The following safety hazards caveat pertains only to the test method portion, Section 7, of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.