【国外标准】 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Manufactured Organic-Base Fibers (Withdrawn 2023)

5.1 The procedures in these test methods should be used with caution for acceptance of commercial shipments owing to the absence of factual information on the between-laboratory precision of many of the test procedures included in these test methods. It is recommended that any program of acceptance testing be preceded by an interlaboratory check in the laboratory of the purchaser and the laboratory of the supplier on replicate specimens of the materials to be tested for each property (or properties) to be evaluated.5.1.1 If there are differences of practical significance between reported test results for two laboratories (or more), comparative tests should be performed to determine if there is a statistical bias between them, using competent statistical assistance. As a minimum, test samples should be used that are as homogeneous as possible, that are drawn from the material from which the disparate test results were obtained, and that are randomly assigned in equal numbers to each laboratory for testing. Other materials with established test values may be used for this purpose. The test results from the two laboratories should be compared using a statistical test for unpaired data, at a probability level chosen prior to the testing series. If a bias is found, either its cause must be found and corrected, or future test results must be adjusted in consideration of the known bias.5.2 The significance and use of particular properties are discussed in the appropriate sections of specific test methods.1.1 These test methods cover the testing of industrial filament yarns made wholly of manufactured organic-base fibers, cords twisted from such yarns, fabrics woven from such cords, and products that are made specifically for use in the manufacture of pneumatic tires. They may be applied to similar yarns and cords used for reinforcing other rubber goods and for other industrial applications. The test methods apply to nylon, polyester, and rayon yarns and tire cords twisted from such yarns and to fabrics made from such cords. The yarn or cord may be wound on cones, tubes, bobbins, spools, or beams; may be woven into fabric; or may be in some other form. The methods include testing procedure only and include no specifications or tolerances.1.2 No procedure is included for the determination of fatigue resistance of cord, but several commonly used procedures for the measurement of fatigue resistance of cords in rubber were published in the appendix of these test methods in the 1967 Annual Book of ASTM Standards, Part 24, and in earlier issues of Test Methods D885.1.3 The sections on “Growth of Conditioned Yarns and Cords,” “Properties of Yarns and Cords at Elevated Temperature,” and “Properties of Wet Yarns and Cords” have been moved to Appendix X1 – Appendix X3 as non-mandatory informational items because of their very limited use by the industry and because precision and bias statements are not included.1.4 This standard includes the following sections:  SectionAdhesion of Cord to Elastomers 34Bibliography of Tire Cord Test Methods X5Breaking Strength (Force) of Yarns and Cords at Elevated Tempera- ture X2.3Breaking Strength (Force) of Conditioned Yarns and Cords 16Breaking Strength (Force) of Oven-Dried Rayon Yarns and Cords 23Breaking Strength (Force) of Rayon Yarns and Cords at Specified Moisture Regain Level, Adjustment of 17Breaking Tenacity of Conditioned Yarns and Cords 18Breaking Tenacity of Oven-Dried Rayon Yarns and Cords 24Breaking Toughness of Yarns and Cords 28Commercial Mass 9Conditioning 7Contraction of Wet Yarns and Cords X3Count of Tire Cord Fabric 37Dip (Adhesive) Solids Pickup on Yarns and Cords 33Elongation at Break of Conditioned Yarns and Cords 19Elongation at Break of Oven-Dried Rayon Yarns and Cords 25Elongation of Rayon Yarns and Cords at a Specified Moisture Regain Level, Adjustment of Observed 20Extractable Matter in Yarns and Cords 32Force at Specified Elongation (FASE) of Conditioned Yarns and Cords 21Force at Specified Elongation (FASE) of Oven-Dried Rayon Yarns and Cords 26Growth of Conditioned Yarns and Cords X1Identification of Fibers 8Keywords 40Linear Density 11Mass of per Unit Area of Tire Cord Fabric 36Modulus of Conditioned Yarns and Cords 22Moisture Regain, Actual 10Precision and Bias of Certain Yarn and Cord Tests 39  35 toProperties of Tire Cord Fabric 38Sampling 6Shrinkage Force of Conditioned Yarns and Cords at Elevated Temper- ature  X2.5Shrinkage of Conditioned Yarns and Cords at Elevated Temperature X2.4, General 5, Tensile Properties 14SI Calculations (examples for work-to-break, specific work-to-break, and breaking toughness)  X4Stiffness of Fabric 38  12 toTensile Properties of Yarns and Cords 28Terminology 3Thickness of Cords 31Twist in Yarns and Cords 30Width of Tire Cord Fabric 35Work-to-Break of Yarns and Cords 271.5 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.