【国外标准】 Standard Specification for Nonoriented Electrical Steel Fully Processed Types

This specification covers the standard requirements for flat-rolled nonoriented fully processed electrical steel intended primarily for commercial power frequency applications in magnetic devices. These electrical steels are low-carbon, silicon iron, or silicon-aluminum-iron alloys that may be made by basic-oxygen, electric-furnace, or other steelmaking practice. Desirable core-loss and permeability characteristics are developed during mill processing, so additional heat treatment is usually not required. The grades contained in this specification have thicknesses of 0.014 in. (0. 36 mm), 0.0185 in. (0.47 mm) and 0.0250 in. (0.64 mm). For a given thickness there are from 7 to 9 types based on the maximum value of core loss measured at 60 Hz and 15 kG (1.5 T) using the Epstein test method. Test methods to determine the required magnetic and mechanical properties are specified. Other typical magnetic and physical properties are listed for reference.1.1 This specification covers the detailed requirements to which flat-rolled nonoriented fully processed electrical steel shall conform.1.2 This steel is produced to specified maximum core-loss values and is intended primarily for commercial power frequency (50 Hz and 60 Hz) applications in magnetic devices. Desirable core-loss and permeability characteristics are developed during mill processing, so additional heat treatment by the user is usually not necessary.1.3 These nonoriented fully processed electrical steels are low-carbon, silicon-iron, or silicon-aluminum-iron alloys containing up to about 3.5 % silicon and a small amount of aluminum.1.4 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to customary (cgs-emu and inch-pound) units which are provided for information only and are not considered standard.1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.