【国外标准】 Standard Test Methods for Thickness of Diffusion Coating
本网站 发布时间:
2024-02-28
开通会员免费在线看70000余条国内标准,赠送文本下载次数,单本最低仅合13.3元!还可享标准出版进度查询、定制跟踪推送、标准查新等超多特权!  
查看详情>>

适用范围:
3.1 A diffusion coating is one produced by causing an element or elements to react with or diffuse into, or both, the surface of a metallic substrate, thus chemically altering the substrate adjacent to the surface. To appreciate the significance of coating thickness measurements one must understand the contributions to a particular coating of solid-solution zones in the substrate and reaction products such as intermetallic compounds.1.1 These test methods cover two procedures for measuring the thickness of diffusion coatings.1.2 Test Method A is the determination of the dimensional-change thickness, defined as the difference in the thickness of the part before and after coating. (The terms micrometer thickness and part growth are considered synonymous with dimensional change thickness.)1.3 Test Method B is the determination of total coating thickness, defined as the distance between the observably unaffected substrate and the exterior surface of the coating. This includes the total of all included phases, zones and layers. (The term case depth is considered to be synonymous with total coating thickness.) The total coating thickness is determined by cross-sectioning the coating, preparing a metallurgical mount and microscopically measuring the coating thickness.1.4 The total coating thickness as determined microscopically from a cross-section will usually be greater than, or equal to, the dimensional change thickness determined by part growth. When the coating is produced primarily by reaction with the substrate, the substrate-coating interface recedes as the substrate is consumed in the reaction. In such cases the difference between the total coating thickness and the dimensional change thickness is the thickness of the substrate consumed.1.5 Diffusion coatings are usually formed at elevated temperatures for service at elevated temperatures. This means that diffusion coatings are dynamic systems which are continually undergoing changes while in an elevated-temperature environment. It is necessary to know that certain phases are growing at the expense of others and to know the previous history of a coating to understand the significance of coating thickness data.1.6 Values in SI units are to be regarded as the standard. Inch-pound units are provided for information only.1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
标准号:
ASTM C664-10(2020)
标准名称:
Standard Test Methods for Thickness of Diffusion Coating
英文名称:
Standard Test Methods for Thickness of Diffusion Coating标准状态:
Active-
发布日期:
-
实施日期:
出版语种:
- 推荐标准
- AS/NZS 1580.481.1.10:1998 (R2013) Paints and related materials - Methods of test Coatings - Exposed to weathering - Degree of flaking and peeling
- AS/NZS 2098.10:1995 Methods of test for veneer and plywood Measurement of dimensions and shape for structural Laminated Veneer Lumber
- AS/NZS 3350.2.10:1996/Amdt 2:2001 Safety of household and similar electrical appliances Particular requirements - Floor treatment machines and wet scrubbing machines
- AS/NZS 3350.2.10:1996/Amdt 3:2007 Safety of household and similar electrical appliances Particular requirements - Floor treatment machines and wet scrubbing machines (IEC 60335-2-10:1992, MOD)
- AS/NZS 3580.9.10:2006 Methods for sampling and analysis of ambient air Determination of suspended particulate matter - PM2.5 low volume sampler - Gravimetric method
- AS/NZS 4266.10:1995 Reconstituted wood-based panels - Methods of test Determination of glue bond durability (boil test)
- AS/NZS 4266.10:1995/Amdt 1:1997 Reconstituted wood-based panels - Methods of test - Determination of glue bond durability (boil test)
- AS/NZS 4695.10.2:1997 Fire hazard testing of electrotechnical products Guidance and test methods for the minimization of the effects of abnormal heat on electrotechnical products involved in fires - Method for testing products made from non-metallic materials for resistance to heat using the ball pressure test
- AS/NZS 4695.2.10:1996 Fire hazard testing of electrotechnical products Test methods - Glow-wire test methods - General
- AS/NZS 60079.10.1:2009/Amdt 1:2013 Explosive atmospheres Classification of areas - Explosive gas atmospheres (IEC 60079-10-1, Ed.1.0(2008) MOD)
- AS/NZS 60695.10.2:2002 Fire hazard testing Guidance and test methods for the minimization of the effects of abnormal heat on electrotechnical products involved in fires - Method for testing products made from non-metallic materials for resistance to heat using the ball pressure test (IEC 60695-10-2:1995, IDT)
- AS/NZS 61241.10:2005/Amdt 1:2007 Electrical apparatus for use in the presence of combustible dust Classification of areas where combustible dusts are or may be present
- AS/NZS ISO 7176.10:2011 Wheelchairs Determination of obstacle-climbing ability of electrically powered wheelchairs
- ASC X9 TR 51-2020 Levies Companion Document Uniform Adoption of X9.129 for Levies Version 3.0
- ASTM 51026-23 Standard Practice for Using the Fricke Dosimetry System